Product Features
Through co-extrusion compounding,the high impact strength,bending resistance and good hardness and abrasion resistance of PC materials are combined to improve the overall toughness of the material;high-definition transparency,high gloss,printability,texture- manufactured.It can get a good streamer and bright glass effect.After hardening,the drop resistance is greatly improved,and there is no signal shielding,which can perfectly replace the glass for the back cover of the mobile phone.
Product Applications
Universal base film for various high pressure and hot pressing IMD/FIM forming processes, such as automotive control parts,interior parts,dashboards,mobile phones,monitors,bags, helmets,hardened for mobile phone back cover,touch screen.
Product Specifications
|
Code
|
Type
|
Color
|
Texture
|
(mm)Thickness
|
(mm)Width
|
|
DFPM12 DFPM11
|
non-impact board
|
Natural
|
Polished/Polished
|
0.070~3.000
(0.003”~0.118”)
|
≤1320 (≤52”)
|
|
DFPM13 DFPM23
|
impact board
|
|
DFPM13 H1 DFPM13 H2
|
harden board
|
|
Gauge Variation
|
d<0.25±10um 0.25≤d≤0.5±15um 0.5<d<1.2±25um d≥1.2±35um
|
Thickness range: 0.175mm、0.2mm、0.25mm;
Customized products available upon inquiries ranging above 0.25mm specifications.
Web width:930mm
Customized width upon request
Physical Properties
|
Items
|
Tes Method
|
Units
|
Value
|
|
PHYSICAL
|
|
Specific Gravity
|
ASTM D792
|
g/cm³
|
1.2
|
|
Light Transmition
|
ASTM D1003
|
%
|
≥90
|
|
Haze
|
ATSM D1003
|
%
|
<0.5
|
|
Yellowness Index
|
ASTM D1925
|
-----
|
<1.0
|
|
M E C H A N I CA L
|
|
Pencil Hardness @750g
|
PMMA
|
ATSM D3363
|
-----
|
HB~H
|
|
Tensile Strength
|
ASTM D882
|
Mpa
|
≥55
|
|
Impact Strength
|
112g Bullet shape
|
mm
|
>100
|
|
Adhesion
|
ATSM D3359
|
-----
|
5B
|
|
THERMAL
|
|
Strain Relief @135℃
|
ASTM D1204
|
%
|
≤1
|
|
Vicat softening point
|
ISO 306/B50
|
℃
|
140
|
Notes: All the above data are acquired by standardized tests, which be used only for the references of the application of products.These data can not be regard as the assurance of physical properties in unstable application of products.